0.97 MPa Structural Silicone Sealant Adhesive For Aluminum 1.41g/Cm3
Product Details:
Place of Origin: | China |
Brand Name: | UNEX |
Certification: | EN1279, GB16776, IGCC-IGMA |
Model Number: | MF881 |
Payment & Shipping Terms:
Minimum Order Quantity: | 1 set |
---|---|
Packaging Details: | Com A 265kg/metal drum, Com B 19kg/barrel |
Delivery Time: | 20-25 work days |
Payment Terms: | T/T, L/C |
Detail Information |
|||
Name: | 0.97 MPa Structural Silicone Sealant Adhesive For Aluminum 1.41g/Cm3 | Base(Com A) Density: | 1.55 ± 0.05 G/cm3 |
---|---|---|---|
Catalyst(Com B) Density: | 1.03 G/cm3 | Mixture By Weight: | (A:B=12:1) |
Mixture By Weight (Viscosity): | 360,000 MPa.S | Mixture By Weight(Application Time(23℃.50%)): | 30-50 Mins |
Hardness Shore A- 4h: | 22 | Hardness Shore A- 24h: | 40 |
Hardness Shore A- 14 Days: | 46 | Adhesion Property At Defnite Elongation: | No Damage |
High Light: | 0.97 MPa silicone adhesive sealant,1.41g/Cm3 silicone adhesive sealant,50mins Structural Adhesive For Aluminum |
Product Description
0.97 MPa Structural Silicone Sealant Adhesive For Aluminum 1.41g/Cm3
DESCRIPTION:
Used for insulating glass, structural glazing, facade and curtain wal system
Excellent adhesion to a wide range of substractes including coated, enamelled and reflective glasses, anodised and polyester paint coated aluminium and stainless steel.
Excellent temperature stability: -80℃ to 180℃
High level of mechanical properties
Hight elasticity and high modulus
Joint movemnets: ±25%
◆ TYPICAL PROPERTIES
TEST ITEMS MEASURED VALUE | ||||
Base(Com A) | Appearance White /Grey Ropy Paste | |||
Density 1.41g/cm3 | ||||
Viscosity 170,000 mPa.S | ||||
Catalyst(Com B) | Appearance Black/White Ropy Paste | |||
Density 1.03 g/cm3 | ||||
Viscosity 80,000 mPa.S | ||||
As mixed | ||||
Mixture By weight(A:B=12:1) | Appearance Black/White/Grey | |||
Density 1.40g/cm3 | ||||
Viscosity 340,000 mPa.S | ||||
Application Time(23℃.50%) 30~50 mins | ||||
Tack-free Time(23℃,50%) 30~60 mins | ||||
Sag | Placed Vertical (50℃) 0 | |||
Placed Horizontal No deformation | ||||
Hardness | Shore A- 24h 35 | |||
Shore A-14 days 44 | ||||
As cured -After 14 days at T 23℃ and 50% RH. | ||||
Tensile Adhesion Strength | 23℃ 0.97 MPa | |||
90℃ 0.85 MPa | ||||
-30℃ 1.84 MPa | ||||
AfterAging in Hot Air 1.01 MPa | ||||
After Water-UV Immersion 0.97 MPa | ||||
Adhesive Failure Area 0% | ||||
23℃ Elongation Under Max.Tensile Strength 140% | ||||
Temperature Resistance -60%~180℃ | ||||
Resistance to UV-Ozone Continuous irradiation under water UV2500 hrs,No change | ||||
Moisture Vapour Transmission Rate (MVTR) 17.7 [gr/m2.24hrs.2mm]-EN1279/4 | ||||
Gas Permeation Rate(Ar) 755x103lgr/m2hrsl.EN1279/4 |